Undoped LiMnPO4 was cycled more than 500 times at 55 °C.
Average capacity loss was less than 0.06% cycle.
After ca 550 cycles very fast capacity degradation was observed.
Surface film formation, Mn dissolution and occurrence of Li4P2O7 was observed.
Decomposition starts at local defects in the microstructure of carbon coating.