A preliminary study on a new LiBOB/acetamide solid phase transition electrolyte

详细信息    查看全文

• 作者：Bin Xie ; Lifei Li ; Hong Li ; Liquan Chen
• 关键词：LiBOB ; Acetamide ; Phase transition electrolyte ; Lithium batteries
• 刊名：Solid State Ionics
• 出版年：2009
• 出版时间：29 May 2009
• 年：2009
• 卷：180
• 期：9-10
• 页码：688-692
• 全文大小：590 K

文摘

New solid electrolytes containing acetamide and lithium bioxalato borate (LiBOB) with different molar ratios have been investigated. Their melting points (T_m) are around 42 °C. The ionic conductivities and activation energies vary drastically below and above T_m, indicating a typical feature of phase transition electrolyte. The ionic conductivity of the LiBOB/acetamide electrolyte with a molar ratio of 1:8 is 5 × 10^− 8 S cm^− 1 at 25 °C but increases to 4 × 10^− 3 S cm^− 1 at 60 °C. It was found that anode materials, such as graphite and Li₄Ti₅O₁₂, could not discharge and charge properly in this electrolyte at 60 °C due to the difficulty in forming a stable passivating layer on the anodes. However, a Li/LiFePO₄ cell with this electrolyte can be charged properly after heating to 60 °C, but cannot be charged at room temperature. Although the LiBOB/acetamide electrolytes are not suitable for Li-ion batteries due to poor electrode compatibility, the current results indicate that a solid electrolyte with a slightly higher phase transition temperature than room temperature may find potential application in stationary battery for energy storage where the electrolyte is at high conductive liquid state at elevated temperature and low conductive solid state at low temperature. The interaction between acetamide and LiBOB in the electrolyte is also studied by Raman and FTIR spectroscopy.