Fifteen-Year Comparison of Wear and Osteolysis Analysis for Cross-Linked or Conventional Polyethylene in Cementless Total Hip Arthroplasty for Hip Dysplasia—A Retrospective Cohort Study

详细信息    查看全文

• 作者：Manabu Tsukamoto ; MD^a ; ; Hideo Ohnishi ; MD ; PhD^b ; Toshiharu Mori ; MD ; PhD^a ; Makoto Kawasaki ; MD ; PhD^a ; Soshi Uchida ; MD ; PhD^c ; Akinori Sakai ; MD ; PhD^a
• 关键词：cementless total hip arthroplasty ; cross-linked polyethylene ; long-term ; wear rate ; osteolysis ; developmental dysplasia of the hip
• 刊名：The Journal of Arthroplasty
• 出版年：2017
• 出版时间：January 2017
• 年：2017
• 卷：32
• 期：1
• 页码：161-165.e1
• 全文大小：533 K
• 卷排序：32

文摘

Cross-linked polyethylene (XLPE) acetabular liners used in cementless total hip arthroplasty (THA) have demonstrated better wear resistance at 10 years compared with conventional polyethylene (CPE) liners. No clinical studies have compared XPLE to CPE liners beyond 10 years.MethodsWe performed a 15-year retrospective cohort study on cementless THA performed in patients with developmental hip dysplasia to measure the differences in polyethylene wear rates and the presence of osteolysis. Twenty-four THAs with XLPE and 17 THAs with CPE were evaluated. The mean age of patients was 55.9 years (41-68) in the XLPE group and 54.4 years (40-67) in the CPE group. The mean follow-up period was 15.1 years (13.9-16.1) in the XLPE group and 15.2 years (14.5-16.0) in the CPE group.ResultsThe XLPE group had a significantly lower wear rate at 5 and 10 years compared with the CPE group; however, no significant difference was found at 15 years (XLPE group, 0.040 mm/y; CPE group, 0.034 mm/y). In addition, the incidence of osteolysis did not differ significantly between the groups. However, the incidence of excessive wear between 10 and 15 years after surgery in the XLPE group was significantly higher than that in the CPE group.ConclusionXLPE demonstrated no advantage in the wear rate or the incidence of osteolysis at 15 years, despite having superior wear resistance up to 10 years. It is concerning that the incidence of excessive wear was higher in the XLPE group between 10 and 15 years, and this finding should alert the arthroplasty community to this possible problem with the more highly cross-linked polyethylene.