文摘
Two different preparation routes were applied to process WC-MgO composites with varying MgO contents (4.1 wt.% and 5.9 wt.% MgO). WC-MgO powder mixtures were synthesized by a milling process at 600 rpm for 6 h of partially oxidized WC (WC + WO3), Mg3N2 and C. Alternatively, WC and MgO as initial powders were used. For consolidation of the powder mixtures the field-assisted sintering technology (FAST) was used. X-ray diffraction shows that samples out of different powder mixtures and sintered between 1600 °C and 1750 °C exhibited WC, MgO and the W2C phase independent of the preparation route of the powder mixtures. A higher density and better mechanical properties (hardness and indentation fracture toughness) of WC-MgO were achieved of pure WC and MgO as initial powders were consolidated by FAST. It was found that a lower MgO content results in higher hardness values and in a slightly decreased indentation fracture toughness.