Low temperature hydrothermal synthesis and magnetic studies of YMnO₃ nanorods

详细信息    查看全文

• 作者：R. Dhinesh Kumar ; R. Jayavel
• 关键词：YMnO3 ; Nanorods ; Magnetic materials ; X-ray techniques
• 刊名：Materials Letters
• 出版年：15 December, 2013
• 年：2013
• 卷：113
• 期：Complete
• 页码：210-213
• 全文大小：1063 K

文摘

In this paper, a facile synthesis of 1D-rodlike Yttrium manganite (YMnO₃) was reported. YMnO₃ nanorods were successfully prepared via a hydrothermal process. The prepared sample was subjected to structural, morphological and magnetic property studies. The XRD pattern confirmed that the prepared sample is phase pure with hexagonal structure. HRSEM, HRTEM and AFM images revealed that the sample contains uniform nanorods with average diameter of 100 nm and length in several micrometers. MFM image shows a magnetic distribution in the rods. The zero-field-cooled (ZFC) and field-cooled (FC) magnetization curve shows an anti-ferromagnetic to paramagnetic transition T_N (Neel temperature) at ~80 K in the temperature range from 20 to 300 K which was further confirmed by magnetic hysteresis loops.