Cr and Mn successfully modified the morphology of Fe-containing intermetallics. Cr- and Mn-dispersoids formed in the aluminium matrix during solution treatment. Dispersion hardening was detected after solution treatment for Cr-containing alloy. The dispersion hardening effect was maintained after ageing treatment.