Low temperature synthesis of nanocrystalline magnesium aluminate with high surface area by surfactant assisted precipitation method: Effect of preparation conditions

详细信息    查看全文

• 作者：Zeinab Mosayebi ; Mehran Rezaei ; Narges Hadian ; Fazlollah Zareie Kordshuli ; Fereshteh Meshkani
• 关键词：A. Ceramics ; A. Nanostructures ; B. Chemical synthesis
• 刊名：Materials Research Bulletin
• 出版年：2012
• 出版时间：September, 2012
• 年：2012
• 卷：47
• 期：9
• 页码：2154-2160
• 全文大小：1714 K

文摘

A surfactant assisted co-precipitation method was employed for the low temperature synthesis of magnesium aluminate spinel with nanocrystalline size and high specific surface area. Pluronic P123 triblock copolymer and ammonia solution were used as surfactant and precipitation agent, respectively. The prepared samples were characterized by thermal gravimetric and differential thermal gravimetric analyses (TG/DTG), X-ray diffraction (XRD), N₂ adsorption (BET) and transmission electron microscopy (TEM) techniques. The effects of several process parameters such as refluxing temperature, refluxing time, pH, P123 to metals mole ratio (P123/metals) and calcination temperature on the structural properties of the samples were investigated. The obtained results showed that, among the process parameters pH and refluxing temperature have a significant effect on the structural properties of samples. The results revealed that increase in pH from 9.5 to 11 and refluxing temperature from 40 ¡ãC to 80 ¡ãC increased the specific surface area of prepared samples in the range of 157-188 m² g^?1 and 162-184 m² g^?1, respectively. The XRD analysis showed the single-phase MgAl₂O₄ was formed at 700 ¡ãC.