Interdiffusion between films during high magnetic field annealing was studied.
XPS results show thickness of diffusion layer increased by magnetic field at 400 K.
Alloying process between films was changed by high magnetic field annealing.
The magnetic properties changed obviously after magnetic field annealing at 400 K.