Carbon/carbon composites were bonded with carbon nanotube/pyrocarbon interlayer.
Carbon nanotube created mechanical interlocking at interlayer-substrate interface.
Carbon nanotube induced annularly stacking of pyrocarbon laminas.
Carbon nanotube increased additional fracture process during shear test.
Carbon nanotube/pyrocarbon-bonded composites possessed excellent shear strength.