蔚-CL-co-LA and 蔚-CL-co-未-VAL copolymers showed semi-alternating (R → 2) or random (R ∼ 1) distribution of sequences.
未-VAL copolymers degraded 3–5 times faster than PCL.
l-LA copolymers had a degradation rate 6–10 times higher than that of PCL.
Their mechanical behavior was heavily dependent on the crystalline phase.
The properties of the copolymers with a low Tm (<52 °C) or a small 螖Hm (<33 J g−1) were not measurable at 37 °C.