Supports with high oxygen lability strongly stabilize iridium nanoparticles at oxidizing conditions.
Iridium nanoparticles on low oxygen lability supports are prone to thermal sintering.
Oxygen ion spillover from the support to particle surface is responsible for sintering resistance.
Ir-catalyzed N2O decomposition intrinsic activity is strongly favored on large iridium particles.