Influence of SAP content and curing age on air void distribution of high performance concrete using 3D volume analysis

详细信息    查看全文

• 作者：Babatunde J. Olawuyi^a ; ^{babatunde@futminna.edu.ng} ; William P. Boshoff^b ; ^{bboshoff@sun.ac.za}
• 关键词：Computed tomography (CT) scanning ; 3D-void analysis ; High-performance concrete ; Air void distribution ; Superabsorbent Polymers (SAP) ; SAP content ; Binder type ; Curing age
• 刊名：Construction and Building Materials
• 出版年：2017
• 出版时间：15 March 2017
• 年：2017
• 卷：135
• 期：Complete
• 页码：580-589
• 全文大小：1287 K
• 卷排序：135

文摘

Incorporating Superabsorbents Polymers (SAP) as internal curing agents (IC-agents) in high performance concrete (HPC) for mitigation of autogenous shrinkage is one new trend in concrete practice. SAP’s water absorption and desorption as cement hydrates however leaves micro voids within the concrete which can negatively influence the mechanical properties of HPC. The SAP content, sizes, binder composition, solid constituents of concrete and curing age could be of direct influence on the resultant air voids sizes and its distribution in concrete. This paper therefore reports on three dimensional (3D) volume analysis of the influence of SAP contents and curing age on air voids distribution in HPC. Four HPC mixtures with different binder constituents and water/binder (W/B): M1F and M1S (0.2), M2 (0.25) and M3 (0.3) were tested with two grain sizes of SAP (SP1 ⩽ 300 μm and SP2 ⩽ 600 μm). The SAP contents were also varied (0%; 0.2%; 0.3%; and 0.4%) by weight of binder. Concrete cylinders (50 mm ϴ × 100 mm) were cast and cured in water for different ages (7, 28, 56 and 90 days) before the hardened HPC was subjected to X-ray computed tomography (CT) scanning for determination of the air void distribution. The analysed 3D X-ray images gave results on SAP grain sizes, SAP air voids, distribution and volume in the HPC with the respective influence of binder type, W/B and curing age assessed.