Effect of montmorillonite on carboxylated styrene butadiene rubber/hindered phenol damping material with improved extraction resistance

详细信息    查看全文

• 作者：Yuan Gao^a ; Xiaoping Wang^a ; ^b ; ^{wangxp@scut.edu.cn" class="auth_mail} ; Meijun Liu^a ; Xue Xi^a ; Xin Zhang^a ; Demin Jia^a
• 关键词：Hindered phenol ; Damping property ; Absorption ; Extraction resistance
• 刊名：Materials and Design
• 出版年：June, 2014
• 年：2014
• 卷：58
• 期：Complete
• 页码：316-323
• 全文大小：925 K

文摘

Three methods of blending, including direct blending, melt blending and latex blending, were introduced to disperse sodium based montmorillonite (Na-MMT) and N,N鈥?hexane-1,6-diylbis{3-(5-di-tert-butyl-4-hydroxyphenyl-propionamide)} (HP1098) into the carboxylated styrene butadiene (XSBR) matrix. Small angle X-ray Diffraction testing indicated that melting Na-MMT with HP1098 enlarged the d-spacing of Na-MMT, which was further enlarged by mechanical blending with XSBR, and this led to homogeneous dispersion of Na-MMT and HP1098, which was indicated by Transmission Electronic Microscopy; latex blending was found most advantageous in dispersing HP1098 which was essential for improved damping performance. Dynamic Mechanical Analysis was utilized to characterize damping properties, and enhanced static mechanical properties were presumably originated from molecule chains being intercalated into the enlarged galleries of Na-MMT by mechanical blending. Formation of hydrogen bonds was observed by Fourier Transformation Infrared Spectrum and was supposed to be responsible for exceptional damping performance at elevated temperature. Extraction measurement of XSBR/Na-MMT/HP1098 composite indicated that XSBR and Na-MMT showed synergic effect in protecting HP1098 molecules from being extracted, which is a promising method in preparing rubber/hindered phenol damping materials with improved extraction resistance, whereby increasing the performance stability and lifespan of the composite materials. Additional advantage of this type of materials is better processability and shortened vulcanization process.