Novel polyaromatic blend membranes containing F6-PBI and phosphine oxide derivatives.
Stability of blend membranes in 80 wt% H2SO4 and 80 wt% H3PO4 for 120 h at 80 °C.
Blend membranes performed comparable to Nafion®115 during SO2 electrolysis.
Performance of MKA16 at 80 °C and 0.1 A cm−2 increased from 0.65 V to 0.75 V after 100 h.