Debinding and sintering behaviors with different nanopowder ratio were analyzed.
Thermal decomposition behavior of binder system was changed by nanopowder.
Apparent debinding activation energy changed proportionally by nanopowder ratio.
Bimodal feedstock showed multi-peak sintering behavior due to nanopowder.
The densification parameter of bimodal feedstocks was higher than micro feedstock.