文摘
In this work, the industrial glass-glass module was developed using bifacial n-type solar cell. The passivation emitter and rear total diffusion cells (PERT) structure solar cell combined boron spin-on with POCl3 diffusion and double sides H-pattern screen printing metallization. With the assistance of the spin-on single side doping method, an average efficiency of 20% with 90% bifaciality was obtained in our laboratory, 6*10 cells bifacial glass-glass modules were fabricated in industrial line. The PID about 3.5% was obtained after 600 hrs under 85°C-85% humidity with a bias of -1000 V, while the LID was about 0.19% under the IEC standard of 60 kW·h/m2 illumination. As expected, power output gains of 15% on sand and 30% on snow were recorded for the glass-glass bifacial modules compared with mono-facial modules in our outdoor experiments.