Precursors to Zn1−xCdxO and (Lu,Y)3Al5O12 oxides were formed under γ-radiation.
Heat treatment was required for wurtzite (ZnO) or garnet (YAG) modification forming.
Phase-pure Zn0.97Cd0.03O solid solution with the maximum Cd content was prepared.
Phase-pure (Lu,Y)3Al5O12:Ce garnets up to 2 M% of Ce were produced.
Crystallite size amounts 50 nm for Zn1−xCdxO and 100 nm for (Lu,Y)3Al5O12.