Li7La3Zr2O12 is a promising electrolyte for rechargeable all solid state batteries.
The stability of low temperature cubic phase of garnet in argon and air was determined.
The garnet stoichiometry was maintained in argon while in air lithium loss occurred.
The influence of CO2 adsorption on the structural modifications of garnet was proved.