The degradation mechanism of h-WO3 when used as the negative electrode in LIB was clarified. The both changes in the crystalline structure and the valence of W of h-WO3 occurred. The deposition of a layer of reactive materials on the surface of the h-WO3 electrode was observed. Changes in the electrolyte composition in LIB occurred.