文摘
Sintering of SnO2 compacts, obtained through slip casting, was studied by means of dilatometry, Hg porosimetry, scanning electron microscopy, and density measurement (Archimedes method). Sintering is strongly influenced by the green microstructure. Moreover, the sintering mechanisms are not dependent on the slurries solid content up to 50 % of solids in volume. Above this value, agglomerates are formed, leading to differential sintering inside and among the agglomerates. Another important point is the reduction of the temperature of maximum shrinkage rate when compared to tin oxide processed by isostatic pressing. This reduction is more accentuated when ammonium hydroxide is added to the suspension.