Two distinct series of binders were designed; the dominant ingredient in the first was calcium sulfate while in the second it was ggbs. Potential applications for both series of binders were considered and the strength development of each binder was analysed. In addition, the effect of water on the gypsum-based binders was analysed, as was the sulfate resistance of the ggbs-based binder.
The results of the laboratory tests carried out were varied. For the calcium sulfate-based binders, those manufactured using anhydrite II as the dominant ingredient were found to achieve highest strengths. However these binders were found to be particularly susceptible to moisture-induced deterioration. For the ggbs-based binders, it was found that the early strength development was improved by the addition of small quantities of anhydrite II and gypsum. The strengths and sulfate resistance at later ages remained unaffected. These binders may have significant potential in situations where early strength development is a requirement.