Microstructure and electrical transport in nano-grain sized Ce0.9Gd0.1O2−δ ceramics
详细信息 查看全文
- 作者：Enrique Ruiz-Trejo ; Jaime Santoyo-Salazar ; Ruben Vilchis-Morales ; Adriana Bení ; tez-Rico ; Francisco Gó ; mez-Garcí ; a ; Carlos Flores-Morales ; José ; Chá ; vez-Carvayar ; Gustavo Taviz
- 关键词：Gd-doped Ceria ; Nanoparticles ; Combustion synthesis ; Nanoceramics ; Conductivity
- 刊名：Journal of Solid State Chemistry
- 出版年：2007
- 出版时间：November 2007
- 年：2007
- 卷：180
- 期：11
- 页码：3093-3100
- 全文大小：657 K
文摘
An enhancement of the electrical conductivity has been found in nano-grain sized Ce0.9Gd0.1O2−δ ceramics when measured in N2 (pO2=3.5×10−6 atm) in comparison with the most commonly accepted values of bulk ionic conductivity. We first present the synthesis and characterisation of the nanoparticles later used for the preparation of dense nanoceramics of Gd-doped CeO2. The nanoparticles were characterised by X-ray diffraction (XRD), atomic force microscopy (AFM) and transmission electron microscopy (TEM). The good sintering properties of these nanopowders allowed us to obtain very dense ceramics (>90 % theoretical density) while keeping the grain size close to 100 nm. The microstructure of these nanoceramics was analysed by AFM and scanning electron microscopy (SEM) while the electrical characterisation was performed by the 4-point dc technique between 500 and 950 °C in air or N2 and ac impedance between 150 and 400 °C in air and or argon. We briefly discuss the possibilities of electron vs. oxygen ion conduction and grain boundary vs. bulk conductivity. The features exhibited by these ceramics represent an increased potential to process solid electroceramics materials with specific levels of electronic and/or ionic conductivities for a variety of electrochemical devices.