Effect of Ni-Mo rich fillers on the control of laves phase in the dissimilar welds. Segregation of Mo rich phases in the inter-dendritic regions. Tensile strength of the weldments was superior than the base metals. Molten salt corrosion studies on the dissimilar joints exposed at 900 °C. Parent metal Inconel 718 exhibited lower corrosion resistance with spallation and blistering of oxide scales.