文摘
Excellent high temperature mechanical properties of melt-grown Al2O3-based eutectics have previously been demonstrated in samples prepared by directional solidification methods. In this study, the deformation behaviour of melt-grown Al2O3/YAG/ZrO2 eutectic bulk prepared by a non-directional solidification method was investigated by means of compressive tests in a temperature range of 1200–1700 °C. The non-directionally solidified eutectic bulk ceramic has a colony structure and is polycrystalline. It begins to show ductility and has a compressive strength of 320 MPa at 1500 °C, which is much higher than that of the sintered ceramic with the same composition. However, its plastic deformability is insufficient, even at 1700 °C (just below the melting point of 1715 °C), and cracking occurs during compressive deformation.