α-Mg Volume fraction was enhanced significantly under rapid solidification.
Complex/quasi regular eutectic structures were developed in Mg-6.8/7.5Li alloys.
Ca can further modify α-Mg configurations in Mg–Li alloys by different mechanisms.
Mg-8.4Li alloy exhibited the highest yield strength due to its distinct structure.