A novel Mg–3RE–6Zn–1.4Y magnesium alloy was designed.
Phase constitutions were distinguished including I, W and T phase.
Increase of pressure refined α-Mg phase and increased solid solubility.
RE-rich intermetallic compounds were homogenized and refined under high pressure.