To achieve the desired temperature profiles and to optimize the parameters involved in the processing of hydrogenated nanocrystalline silicon (nc-Si:H) films with the UV-ELA, a numerical analysis by finite element method (FEM) of a multilayer structure has been performed. The multilayer structures, consisting of thin alternating a-Si:H(10 nm) and n-doped nc-Si:H(60 nm) layers, deposited on a glass substrate, has also been experimentally analyzed.
Temperature profiles caused by 193 nm radiation with 25 ns pulse length and energy densities ranging from 50 mJ/cm2 to 400 mJ/cm2 have been calculated. Numerical results allowed us to estimate the dehydrogenation process of the different layers and the diffusion of phosphorous (P) in Si layers as well as their structural modifications as a function of the applied laser energy density. Numerical results are compared with exhaustive characterization of the experimental results.