Glass–alumina composite coatings by plasma spraying. Part II: Microstructure-based modeling of mechanical properties
详细信息    查看全文
文摘
The mechanical properties of composite glass–alumina coatings produced by plasma spraying, as described in Part I, were numerically characterized with relation to the peculiar microstructure. Finite element meshes were created for the most significant coating typologies, starting from SEM acquired microstructures. The coatings elastic properties and fracture behaviour were characterized as a function of relevant microstructural features. The results confirm that the coatings are anisotropic, with a lower elastic modulus in the direction perpendicular to the substrate plane (spray direction), because of the lamellar microstructure; increasing the alumina volume fraction increases the elastic modulus value both in the spray and transverse direction. Moreover, it is found that cracks start from large, irregular pores, and propagate easily through the glass areas, but are stopped by alumina. Smaller individual glass areas hinder crack propagation. The post-deposition thermal treatment described in Part I produces tensile residual stresses in the glass and compressive ones in the alumina; thus, the arresting effect of the latter on cracks propagation is greatly enhanced.

© 2004-2018 中国地质图书馆版权所有 京ICP备05064691号 京公网安备11010802017129号

地址:北京市海淀区学院路29号 邮编:100083

电话:办公室:(+86 10)66554848;文献借阅、咨询服务、科技查新:66554700