Isothermal sections of the U-Nb-Al system were investigated for 900 K and 1200 K.
The formation reaction of the intermediate phases was determined.
The crystallographic properties of the equilibrium phases were checked.
The thermodynamic properties was modelized by CALPHAD method.
The electronic properties of the intermediate phases were investigated.