文摘
By employing conductive and transparent La0.07Ba0.93SnO3 (LBSO) films as bottom electrodes, epitaxial BiFe0.95Mn0.05O3 (BFMO) ferroelectric capacitors were fabricated on SrTiO3(0 0 1) [STO(0 0 1)] substrates by pulsed laser deposition method. The LBSO films showed an excellent optical transmittance in the visible range and a weak metallic conductive behavior, with the room-temperature resistivity, carrier concentration, and mobility of 1.223 m¦¸ cm, 5.54 ¡Á 1021 cm?3, and 0.923 cm2/V s, respectively. X-ray photoelectron spectroscopy and X-ray absorption near-edge structure spectra analysis revealed that iron ions were present primarily as Fe3+ in BFMO films. The band gap of BFMO films was determined to be 2.63 eV from the optical transmittance of the BFMO/LBSO/STO(0 0 1) heterostructures. Pt/BFMO/LBSO/STO(0 0 1) structured ferroelectric thin-film capacitors showed well-saturated rectangular-shaped polarization-electric field hysteresis loops with the remanent polarization of 45 ¦ÌC/cm2 at a measurement frequency of 1 kHz, indicating that the perovskite-type LBSO films can be potentially used in transparent devices especially based on all-perovskite heterostructures.