Multi-field modelling of hydride forming metals Part II: Application to fracture
详细信息    查看全文
文摘
In Part I of the present article, we formulated a continuum-based computational model for stress- and temperature-directed diffusion of hydrogen in metals that form brittle binary hydrides, such as Zr and Ti alloys. Among the space-time dependent parameters calculated by the model are the volume fraction and the mean orientation of hydride precipitates. These parameters are of importance for quantifying the embrittlement of hydrided materials. In this second part of the work, we use measured data for the strength and toughness of hydrided Zr alloys to correlate the local fracture properties of the two-phase (metal + hydride) material to the aforementioned parameters. The local fracture properties are used as space-time dependent input to a cohesive zone type submodel for fracture, which is fully integrated with the hydrogen transport model from Part I. The complete model is validated against fracture tests on hydrogen-charged Zr-2.5%Nb, a material used in nuclear reactor pressure tubes. More precisely, we study local embrittlement and crack initiation at a blunt and moderately stressed notch, resulting from gradual accumulation of hydrides at the notch during temperature cycling. We also simulate tests on crack initiation and growth by delayed hydride cracking, a subcritical crack growth mechanism with a complex temperature dependence. From the results of the simulations, we conclude that the model reproduces many observed features related to initiation and propagation of hydride induced cracks in the Zr-2.5%Nb material. In particular, it has the capacity to reproduce effects of the material鈥檚 temperature history on the fracture behaviour, which is important for many practical applications.

© 2004-2018 中国地质图书馆版权所有 京ICP备05064691号 京公网安备11010802017129号

地址:北京市海淀区学院路29号 邮编:100083

电话:办公室:(+86 10)66554848;文献借阅、咨询服务、科技查新:66554700