Synthesis of nanocrystalline TaC powders via single-step high temperature spray pyrolysis from solution precursors

详细信息    查看全文

• 作者：Zhe Cheng^a ; ^b ; ^{zhcheng@fiu.edu} ; Paniz Foroughi^a ; ^b ; André ; s Behrens^a ; ^b
• 关键词：Spray pyrolysis ; Nanoparticles ; Ultra-high temperature ceramics ; Precursors ; Reduction
• 刊名：Ceramics International
• 出版年：2017
• 出版时间：15 February 2017
• 年：2017
• 卷：43
• 期：3
• 页码：3431-3434
• 全文大小：1124 K
• 卷排序：43

文摘

Nanocrystalline powders for high temperature ceramics (HTC) and ultrahigh temperature ceramics (UHTC) are important materials for aerospace and other important industrial applications. In this study, a low cost, single-step synthesis method for nanocrystalline HTC and UHTC powders is reported, which is based on high temperature spray pyrolysis (HTSP) process. The synthesis starts with solution of oxide and carbon precursors dissolved in common organic solvents, which are broken into fine droplets (e.g., via nebulizer). The droplets then go through processes of solvent removal, thermolysis, and rapid in situ carbothermal reduction (CTR), all in one single pass in a tube furnace operated at high temperature. The synthesis method was demonstrated successfully using the example of tantalum carbide (TaC) from precursors of tantalum chloride (TaCl5) and phenolic resin in a single-step HTSP process with maximum temperature of 1650 °C in one pass that finished within minutes, yielding agglomerated nanocrystalline TaC UHTC powders.