Production of multi-, oligo- and single-pore membranes using a continuous ion beam

详细信息    查看全文

• 作者：P.Yu. Apel^a ; ^b ; ^{apel@nrmail.jinr.ru" class="auth_mail" title="E-mail the corresponding author} ; O.M. Ivanov^a ; N.E. Lizunov^a ; T.I. Mamonova^a ; A.N. Nechaev^a ; K. Olejniczak^a ; ^c ; J. Vacik^d ; S.N. Dmitriev^a
• 关键词：Ion beam ; Irradiation ; Ion track ; Etching ; Single nanopore
• 刊名：Nuclear Instruments and Methods in Physics Research Section B: Beam Interactions with Materials and Atoms
• 出版年：2015
• 出版时间：15 December 2015
• 年：2015
• 卷：365
• 期：part_PB
• 页码：641-645
• 全文大小：1577 K

文摘

Ion track membranes (ITM) have attracted significant interest over the past two decades due to their numerous applications in physical, biological, chemical, biochemical and medical experimental works. A particular feature of ITM technology is the possibility to fabricate samples with a predetermined number of pores, including single-pore membranes.

The present report describes a procedure that allowed for the production of multi-, oligo- and single-pore membranes using a continuous ion beam from an IC-100 cyclotron. The beam was scanned over a set of small diaphragms, from 17 to ∼1000 μm in diameter. Ions passed through the apertures and impinged two sandwiched polymer foils, with the total thickness close to the ion range in the polymer. The foils were pulled across the ion beam at a constant speed. The ratio between the transport speed and the scanning frequency determined the distance between irradiation spots. The beam intensity and the aperture diameters were adjusted such that either several, one or no ions passed through the diaphragms during one half-period of scanning. After irradiation, the lower foil was separated from the upper foil and was etched to obtain pores 6–8 μm in diameter. The pores were found using a color chemical reaction between two reagents placed on opposite sides of the foil. The located pores were further confirmed using SEM and optical microscopy. The numbers of tracks in the irradiation spots were consistent with the Poisson statistics. Samples with single or few tracks obtained in this way were employed to study fine phenomena in ion track nanopores.