Microchemical and microstructural studies in a PTA weld overlay of Ni–Cr–Si–B alloy on AISI 304L stainless steel

详细信息    查看全文

• 作者：C. Sudha ; P. Shankar ; R.V. Subba Rao ; R. Thirumurugesan ; M. Vijayalakshmi ; Baldev Raj
• 关键词：Chemical repartitioning ; Chromium boride ; Interdiffusion zone ; Ni– ; Cr– ; Si– ; B alloy coating ; PTA
• 刊名：Surface and Coatings Technology
• 出版年：2008
• 出版时间：15 February 2008
• 年：2008
• 卷：202
• 期：10
• 页码：2103-2112
• 全文大小：1791 K

文摘

Ni–Cr–Si–B alloy coatings deposited on AISI 304L stainless steel substrate using plasma transferred arc welding process were studied with respect to the microchemical and microstructural modifications that take place during the process. The coating was characterized for (1) interface integrity and dilution (2) type, morphology and distribution of secondary phases in the coating (3) elemental redistribution between substrate and coating and (4) different phases that form during the deposition process. Formation of a transition zone of only 760 μm width was understood in terms of interdiffusion of Fe and Ni across the interface. Preferential redistribution of carbon to the surface of the coating was observed. It was explained on the basis of difference in thermodynamic activity. Apart from γ-Ni solid solution, the other primary phases identified in Ni–Cr–Si–B alloy were Cr₂B, Cr₇C₃ and Cr₃C₂. The observed changes in microstructure, microchemistry and hardness have been understood based on the phase transitions of the Ni rich alloy during solidification and cooling on the substrate.