Cracking of 2.25Cr–1.0Mo steel tube/stationary tube-sheet weldment of a heat-exchanger

详细信息    查看全文

• 作者：C.R.F. Azevedo ; F. Beneduce Neto ; S.D. Br ; i ; A.P. Tschiptschin
• 关键词：Heat-exchanger ; 2.25Cr– ; 1.0Mo steel ; Welding ; Transversal cracking ; Intergranular oxidation
• 刊名：Engineering Failure Analysis
• 出版年：2008
• 出版时间：September 2008
• 年：2008
• 卷：15
• 期：6
• 页码：695-710
• 全文大小：3895 K

文摘

The premature failure of a horizontal heat-exchanger, which occurred after service exposure at 580 °C for 50,000 h, revealed the occurrence of extensive through-thickness cracking in approximately 40 % of the tube/stationary tube-sheet welds. Additionally, the internal surface of the welded joint featured intensive secondary intergranular cracking (up to 250 μm deep), preferential formation of a 150 μm thick layer of (Fe,Cr)₃O₄ and internal intergranular oxidation (40 μm deep). The welded region also showed intense carbon pick-up and, as consequence, severe precipitation of intergranular M₇C₃ and M₂₃C₆ carbides. The fracture surface was composed of two distinct regions: a “planar” region of 250 μm, formed due to the stable crack growth along by the intergranular oxidation; and a slant region with radial marks, formed by the fast crack growth along the network of intergranular carbides. The association of intergranular oxidation pre-cracks with microstructural embrittlement promoted the premature failure, which took place by an overload mechanism, probably due to the jamming of the floating tube-sheet during the maintenance halt (cooling operation).