Thermal stability of tungsten sub-nitride thin film prepared by reactive magnetron sputtering

详细信息    查看全文

• 作者：X.X. Zhang^a ; ^c ; Y.Z. Wu^a ; ^{youzhiwu@163.com} ; B. Mu^b ; L. Qiao^c ; W.X. Li^d ; J.J. Li^d ; P. Wang^c ; ^{pengwang@licp.cas.cn}
• 关键词：Magnetron sputtering ; Tungsten sub-nitride ; Thermal stability ; Structure ; Annealing ; Thermal desorption spectroscopy
• 刊名：Journal of Nuclear Materials
• 出版年：2017
• 出版时间：March 2017
• 年：2017
• 卷：485
• 期：Complete
• 页码：1-7
• 全文大小：2095 K
• 卷排序：485

文摘

Tungsten sub-nitride thin films deposited on silicon samples by reactive magnetron sputtering were used as a model system to study the phase stability and microstructural evolution during thermal treatments. XRD, SEM&FIB, XPS, RBS and TDS were applied to investigate the stability of tungsten nitride films after heating up to 1473 K in vacuum. At the given experimental parameters a 920 nm thick crystalline film with a tungsten and nitrogen stoichiometry of 2:1 were achieved. The results showed that no phase and microstructure change occurred due to W2N film annealing in vacuum up to 973 K. Heating up to 1073 K led to a partial decomposition of the W2N phase and the formation of a W enrichment layer at the surface. Increasing the annealing time at the same temperature, the further decomposition of the W2N phase was negligible. The complete decomposition of W2N film happened as the temperature reached up to 1473 K.