Screen printed carbon nanotube thick film on alumina substrate

详细信息    查看全文

• 作者：Varsha D. Phadtare^a ; Vinayak G. Parale^b ; Gopal K. Kulkarni^a ; Ninad B. Velhal^a ; Hyung-Ho Park^b ; Vijaya R. Puri^a ; ^{vrp_phy@unishivaji.ac.in}
• 关键词：Multiwalled carbon nanotubes ; Thick film ; Microwave permittivity
• 刊名：Ceramics International
• 出版年：2017
• 出版时间：1 April 2017
• 年：2017
• 卷：43
• 期：5
• 页码：4612-4617
• 全文大小：1164 K
• 卷排序：43

文摘

In the present study, the properties of screen printed multiwalled carbon nanotube(MWCNT) thick film on alumina substrate has been reported. Adherent thick film of thickness 10 µm was obtained for the first time by the screen printing method. Thermo gravimetric and differential thermal analysis shows that carbon nanotubes were thermally stable in nitrogen atmosphere upto 750 °C. X ray diffraction pattern shows two characteristic peaks at about 26.5°and 54.7°, corresponding to (002) and (004) reflections of graphite structure, respectively. Due to the functionalization process agglomeration of MWCNT was reduced and mesh like surface morphology with non-uniform surface was observed by scanning electron micrograph. The calculated values of real and imaginary microwave permittivity of MWCNT thick film from the straight resonator overlay method are 6.6 and 17.6 respectively