文摘
This paper reports a novel nonlinear optical polymer BP-AVT-TCV functionalized with a thiophene- and tricyanovinyl-substituted chromophore. BP-AVT-TCV was synthesized by the post-tricyanovinylation of an epoxy-based precursor polymer BP-AVT, and had a high molar functionalization degree of chromophore (70 mol. % ). It had an enhanced glass transition temperature (Tg = 164 °C) compared with BP-AVT (Tg = 114 °C), and a high decomposition temperature (Td,5 % = 295 °C). BP-AVT-TCV was further cross-linked to achieve the three-dimensional (3D) network of thermosetting polyurethane (PU). The poled PU films revealed an electro-optic (EO) coefficient (γ33) value of 21 pm/V at a wavelength of 1315 nm. The structures of the polymers were confirmed by FT-IR, UV–Vis, and 1H NMR spectra.