文摘
Through arc smelting and high energy ball milling method to synthesized the powders of LaxNd2-xFe17 (x=0.0, 0.2, 0.4, 0.6). By x-ray diffraction (XRD), scanning electron microscopy (SEM) and laser particle analyzer (LPS) to study the structural, morphology, particle size distribution of the powders, respectively. The electromagnetic parameters and saturation magnetization of the powers were measured by a vector network analyzer (VNA) and vibrating sample magnetometer (VSM), respectively. The saturation magnetization decreases with the La increasing. The minimum absorption peak frequency shifts towards a lower frequency region with an increase of La concentration. The microwave absorbing properties of the composite with different ratios of La0.2Nd1.8Fe17/Ni were studied. The microwave absorbing peaks of the composite shift to higher frequencies, and the microwave absorbing properties improved with the Ni content increase to 20%. The minimum reflection loss is −32.5 dB at 9.8 GHz and the bandwidth less than −10 dB (Microwave absorption rate 90%) reaches 3 GHz with a thickness of 1.8 mm.