Films with highly c-axis orientation and optical transparency (60–80%).
Three electronic transitions were uniquely assigned.
The direct transitions are the dominant effect for CuCrO2 optical properties.
Infrared active modes (Eu↑ and A2u↑) can be inferred.
The film density and Hall mobility decrease with increasing annealing temperature.