Excellent ductility with increasing strength was achieved via multi-pass rolling.
High yield strengths were following slip-dominated Hall–Petch relations.
Enhanced uniform elongation was correlated with improved strain-hardening rate.
Post-necking elongation was weakened by restriction of dynamic recovery.