Shot peening (SP) was trialled on AISI 316L before sequential plasma processes. SP prior to sequential plasma processes increased the near-surface hardness. Shot peening (SP) also increased thicknesses of carburized and nitrided layers. Superior wear resistance was achieved by SP and plasma processes at 475 °C. SP partially counteracted the deleterious effect of chromium nitrides on corrosion.