Li5Cr9Ti4O24 nanocrystalline is prepared by a sol-gel route.
Li5Cr9Ti4O24 nanocrystalline shows excellent electrochemical property.
Li5Cr9Ti4O24 nanocrystalline retains 100% capacity retention after 200 cycles.
Structural change of Li5Cr9Ti4O24 nanocrystalline is studied by in-situ XRD.