Removal of mercury (II) and chromium (VI) from wastewater using a new and effective composite: Pumice-supported nanoscale zero-valent iron

详细信息    查看全文

• 作者：Tingyi Liu^a ; Zhong-Liang Wang^a ; ^b ; ^{wangzhongliang@vip.skleg.cn" class="auth_mail} ; Xiaoxing Yan^a ; Bing Zhang^a
• 关键词：Pumice ; Nanoscale zero-valent iron ; Chromium (VI) ; Mercury (II)
• 刊名：Chemical Engineering Journal
• 出版年：1 June, 2014
• 年：2014
• 卷：245
• 期：Complete
• 页码：34-40
• 全文大小：1270 K

文摘

Nanoscale zero-valent iron successfully supported on pumice (P-NZVI) was used to remove heavy metals from wastewater with a higher removal capacity and efficiency. NZVI particles with a mean diameter of 30.6 nm are distributed uniformly on the surface of P-NZVI. The thermal stability and mechanical strength of P-NZVI were also obviously enhanced. P-NZVI with a 7.7% NZVI mass fraction had a specific surface area (S_BET) of 32.2 m²/g. The removal capacity of Hg (II) and Cr (VI) by P-NZVI was 332.4 mg Hg/g Fe and 306.6 mg Cr/g Fe, respectively. As an increase of pH, the removal rates of Hg (II) increased but those of Cr (VI) decreased gradually. P-NZVI is a regenerated material. The X-ray photoelectron spectroscope analysis (XPS) results indicated that Hg (II) and Cr (VI) were removed by a rapid physical adsorption in the first 0.5 min and predominantly by reduction. In terms of the efficiency and speed, P-NZVI was a promising candidate for applications to in situ environmental remediation, especially to the heavy metals pollution incidents with an extremely high concentration of heavy metals.