A Cf/BMI composite experienced high temperature exposure and remained favorable mechanical performance. Thermal ageing degraded static mechanical properties by inducing decomposition, interface debonding and microcracks. A modified C-scan technique was valid in determining efficiency of absorbed energy and impact failure mechanism. Thermal ageing enhanced critical transition from barely impact damage to visually detectable impact damage. Barely visible impact damage characteristics and corresponding mechanism of aged composite were revealed.