BNSO films were epitaxially grown on MgO substrates by pulsed laser deposition.
The lowest room temperature resistivity value of 4.81 × 10−4 Ω cm was obtained.
All the films exhibit a high transmittance of more than 80% in the visible range.
The variation of Eg with Nb doping content was explained by Burstein-Moss effect.