In situ deuterium observation in deuterium-implanted tungsten

详细信息    查看全文

• 作者：Yoshinori Furuta ; Ikuji Takagi ; Shotaro Kawamura ; Kazuyoshi Yamamichi ; Masafumi Akiyoshi ; Takayuki Sasaki ; Taishi Kobayashi
• 关键词：Tungsten ; Deuterium ; Trap ; Recombination ; NRA ; Implantation
• 刊名：Nuclear Instruments and Methods in Physics Research Section B: Beam Interactions with Materials and Atoms
• 出版年：15 November, 2013
• 年：2013
• 卷：315
• 期：Complete
• 页码：121-125
• 全文大小：932 K

文摘

In order to evaluate the tritium inventory in plasma-facing tungsten components of a fusion reactor, deuterium depth profiles in tungsten were observed in situ using nuclear reaction analysis (NRA) under continuous implantation of 3 keV D ions. Measurements were conducted at temperatures of 384, 473, 573 and 673 K. Recombination coefficients and rate constants for the surface recombination process were estimated from the observed deuterium concentration. It is indicated that the measured surface recombination rate constant is applied in a case wherein tungsten is exposed to hydrogen particles of various energies from a fusion plasma. The measured recombination coefficient was identical to that found by a different technique in a previous work. Deuterium in trap sites was found to contribute to deuterium retention in the samples as well as to deuterium in solution sites. The deuterium retention was low in the 384 K sample, in which trap sites had not appeared. Deuterium retention was very low in the 673 K sample, where most deuterium atoms were detrapped and desorbed. At an intermediate temperature of 473 K, the retention showed a maximum value due to a large occupancy of deuterium over many trap sites. The dependence of the retention on deuterium fluence was explained assuming that trap sites were produced by implantation.