Induced surface defects reduced HCF and VHCF strength by 40% for a structural steel.
Strength degradation by defect (size 100–300 μm) was described by available models.
FGA in VHCF crack initiation region from inclusion was a layer of nanograins.
No evidence of grain refinement in VHCF crack initiation at GB or at surface defect.