Study on the formation during the production of lead-free piezoceramics at the morphotropic phase boundary

详细信息    查看全文

• 作者：Amauri J. Paula ; Rodrigo Parra ; Maria A. Zaghete ; José ; A. Varela
• 关键词：A. Ferroelectrics ; D. Piezoelectricity ; D. Electrostriction ; D. Dielectric response
• 刊名：Solid State Communications
• 出版年：2009
• 出版时间：October 2009
• 年：2009
• 卷：149
• 期：39-40
• 页码：1587-1590
• 全文大小：2316 K

文摘

Because of the environmental concerns, the manufacture of ceramics based on lead titanate zirconate [Pb(Zr_1−xTi_x)O₃−PZT] has been condemned because of the lead toxicity. In this context, the electromechanical properties of sodium, potassium and lithium niobate [(Na_0.5−x/2K_0.5−x/2Li_x)NbO₃−NKLN] at the morphotropic phase boundary granted these materials the position of most suitable candidate to replace PZT. However, the production of these ceramics is rather critical mainly because of a natural tendency of forming secondary phases. To help with the studies of the synthesis of this lead-free piezoceramic, this work presents an evaluation of the crystallization of the (Na_0.47K_0.47Li_0.06)NbO₃ phase by solid-state reactions. TG-DTA, XRD, dilatometric and ferroelectric hysteresis analyses indicated that a secondary phase (K₃Li₂Nb₅O₁₅) crystallizes at temperatures above 850 C and also during the sintering of the powders compacts at 1080 C. To prevent the formation of this phase, the addition of Na₂Nb₂O₆.nH₂O microfibers obtained through a microwave hydrothermal synthesis was performed in the sintering process. After to this addition, the suppression of the K₃Li₂Nb₅O₁₅ phase occurred and an increase of the NKLN electrical properties was then obtained.