High-temperature deformation behavior of a WE magnesium alloy was investigated through MAF. PSN occurred due to the presence of Mg24Y5 eutectic phases. A texture weakening was realized by applying MAF. The excellent room temperature ductility was achieved as a result of texture weakening.